358.0 Aluminum vs. N06603 Nickel
358.0 aluminum belongs to the aluminum alloys classification, while N06603 nickel belongs to the nickel alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 358.0 aluminum and the bottom bar is N06603 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 190 |
| Elongation at Break, % | 3.5 to 6.0 | |
| 28 |
| Fatigue Strength, MPa | 100 to 110 | |
| 230 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 27 | |
| 76 |
| Shear Strength, MPa | 300 to 320 | |
| 480 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 370 | |
| 740 |
| Tensile Strength: Yield (Proof), MPa | 290 to 320 | |
| 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 520 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 1000 |
| Melting Completion (Liquidus), °C | 600 | |
| 1340 |
| Melting Onset (Solidus), °C | 560 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 480 |
| Thermal Conductivity, W/m-K | 150 | |
| 11 |
| Thermal Expansion, µm/m-K | 21 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 50 |
| Density, g/cm3 | 2.6 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 8.4 |
| Embodied Energy, MJ/kg | 160 | |
| 120 |
| Embodied Water, L/kg | 1090 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 20 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 590 to 710 | |
| 300 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 53 | |
| 24 |
| Strength to Weight: Axial, points | 37 to 39 | |
| 25 |
| Strength to Weight: Bending, points | 42 to 44 | |
| 22 |
| Thermal Diffusivity, mm2/s | 63 | |
| 2.9 |
| Thermal Shock Resistance, points | 16 to 17 | |
| 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 89.1 to 91.8 | |
| 2.4 to 3.0 |
| Beryllium (Be), % | 0.1 to 0.3 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.2 to 0.4 |
| Chromium (Cr), % | 0 to 0.2 | |
| 24 to 26 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 0.3 | |
| 8.0 to 11 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.15 |
| Nickel (Ni), % | 0 | |
| 57.7 to 65.6 |
| Phosphorus (P), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 7.6 to 8.6 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0.1 to 0.2 | |
| 0.010 to 0.25 |
| Yttrium (Y), % | 0 | |
| 0.010 to 0.15 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0.010 to 0.1 |
| Residuals, % | 0 to 0.15 | |
| 0 |