359.0 Aluminum vs. 6101B Aluminum
Both 359.0 aluminum and 6101B aluminum are aluminum alloys. They have a moderately high 91% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 359.0 aluminum and the bottom bar is 6101B aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 68 |
| Elongation at Break, % | 3.8 to 4.9 | |
| 9.1 to 13 |
| Fatigue Strength, MPa | 100 | |
| 62 to 70 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Shear Strength, MPa | 220 to 230 | |
| 120 to 150 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 350 | |
| 190 to 250 |
| Tensile Strength: Yield (Proof), MPa | 250 to 280 | |
| 140 to 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 530 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 600 | |
| 640 |
| Melting Onset (Solidus), °C | 570 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 910 | |
| 900 |
| Thermal Conductivity, W/m-K | 140 | |
| 210 |
| Thermal Expansion, µm/m-K | 21 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 57 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 190 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.6 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1090 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 15 | |
| 20 to 23 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 to 540 | |
| 140 to 240 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 54 | |
| 50 |
| Strength to Weight: Axial, points | 37 to 38 | |
| 20 to 25 |
| Strength to Weight: Bending, points | 42 to 43 | |
| 27 to 32 |
| Thermal Diffusivity, mm2/s | 59 | |
| 87 |
| Thermal Shock Resistance, points | 16 to 17 | |
| 8.5 to 11 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 88.9 to 91 | |
| 98.2 to 99.3 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 0.2 | |
| 0.1 to 0.3 |
| Magnesium (Mg), % | 0.5 to 0.7 | |
| 0.35 to 0.6 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.050 |
| Silicon (Si), % | 8.5 to 9.5 | |
| 0.3 to 0.6 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.1 |