364.0 Aluminum vs. 3102 Aluminum
Both 364.0 aluminum and 3102 aluminum are aluminum alloys. They have a moderately high 90% of their average alloy composition in common.
For each property being compared, the top bar is 364.0 aluminum and the bottom bar is 3102 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 69 |
| Elongation at Break, % | 7.5 | |
| 23 to 28 |
| Fatigue Strength, MPa | 120 | |
| 31 to 34 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Shear Strength, MPa | 200 | |
| 58 to 65 |
| Tensile Strength: Ultimate (UTS), MPa | 300 | |
| 92 to 100 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 28 to 34 |
Thermal Properties
| Latent Heat of Fusion, J/g | 520 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 180 |
| Melting Completion (Liquidus), °C | 600 | |
| 640 |
| Melting Onset (Solidus), °C | 560 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 120 | |
| 230 |
| Thermal Expansion, µm/m-K | 21 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 56 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 190 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.0 |
| Density, g/cm3 | 2.6 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1080 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 | |
| 16 to 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 5.8 to 8.3 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 53 | |
| 50 |
| Strength to Weight: Axial, points | 31 | |
| 9.4 to 10 |
| Strength to Weight: Bending, points | 38 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 51 | |
| 92 |
| Thermal Shock Resistance, points | 14 | |
| 4.1 to 4.4 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 87.2 to 92 | |
| 97.9 to 99.95 |
| Beryllium (Be), % | 0.020 to 0.040 | |
| 0 |
| Chromium (Cr), % | 0.25 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 1.5 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0.2 to 0.4 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0.050 to 0.4 |
| Nickel (Ni), % | 0 to 0.15 | |
| 0 |
| Silicon (Si), % | 7.5 to 9.5 | |
| 0 to 0.4 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.15 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |