383.0 Aluminum vs. 514.0 Aluminum

Both 383.0 aluminum and 514.0 aluminum are aluminum alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is 383.0 aluminum and the bottom bar is 514.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 75
50
Elastic (Young's, Tensile) Modulus, GPa 73
68
Elongation at Break, % 3.5
7.3
Fatigue Strength, MPa 150
48
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 28
25
Tensile Strength: Ultimate (UTS), MPa 280
180
Tensile Strength: Yield (Proof), MPa 150
74

Thermal Properties

Latent Heat of Fusion, J/g 540
400
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 580
640
Melting Onset (Solidus), °C 540
610
Specific Heat Capacity, J/kg-K 880
900
Thermal Conductivity, W/m-K 96
140
Thermal Expansion, µm/m-K 21
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 23
35
Electrical Conductivity: Equal Weight (Specific), % IACS 74
120

Otherwise Unclassified Properties

Base Metal Price, % relative 10
9.5
Density, g/cm3 2.8
2.7
Embodied Carbon, kg CO2/kg material 7.5
8.9
Embodied Energy, MJ/kg 140
150
Embodied Water, L/kg 1030
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 8.2
11
Resilience: Unit (Modulus of Resilience), kJ/m3 150
41
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 50
51
Strength to Weight: Axial, points 28
19
Strength to Weight: Bending, points 34
26
Thermal Diffusivity, mm2/s 39
57
Thermal Shock Resistance, points 13
7.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 79.7 to 88.5
93.6 to 96.5
Copper (Cu), % 2.0 to 3.0
0 to 0.15
Iron (Fe), % 0 to 1.3
0 to 0.5
Magnesium (Mg), % 0 to 0.1
3.5 to 4.5
Manganese (Mn), % 0 to 0.5
0 to 0.35
Nickel (Ni), % 0 to 0.3
0
Silicon (Si), % 9.5 to 11.5
0 to 0.35
Tin (Sn), % 0 to 0.15
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0 to 3.0
0 to 0.15
Residuals, % 0 to 0.5
0 to 0.15