383.0 Aluminum vs. EN AC-43300 Aluminum

Both 383.0 aluminum and EN AC-43300 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is 383.0 aluminum and the bottom bar is EN AC-43300 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 75
91 to 94
Elastic (Young's, Tensile) Modulus, GPa 73
71
Elongation at Break, % 3.5
3.4 to 6.7
Fatigue Strength, MPa 150
76 to 77
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 28
27
Tensile Strength: Ultimate (UTS), MPa 280
280 to 290
Tensile Strength: Yield (Proof), MPa 150
210 to 230

Thermal Properties

Latent Heat of Fusion, J/g 540
540
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 580
600
Melting Onset (Solidus), °C 540
590
Specific Heat Capacity, J/kg-K 880
910
Thermal Conductivity, W/m-K 96
140
Thermal Expansion, µm/m-K 21
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 23
40
Electrical Conductivity: Equal Weight (Specific), % IACS 74
140

Otherwise Unclassified Properties

Base Metal Price, % relative 10
9.5
Density, g/cm3 2.8
2.5
Embodied Carbon, kg CO2/kg material 7.5
7.9
Embodied Energy, MJ/kg 140
150
Embodied Water, L/kg 1030
1080

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 8.2
9.1 to 17
Resilience: Unit (Modulus of Resilience), kJ/m3 150
300 to 370
Stiffness to Weight: Axial, points 15
15
Stiffness to Weight: Bending, points 50
54
Strength to Weight: Axial, points 28
31 to 32
Strength to Weight: Bending, points 34
37 to 38
Thermal Diffusivity, mm2/s 39
59
Thermal Shock Resistance, points 13
13 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 79.7 to 88.5
88.9 to 90.8
Copper (Cu), % 2.0 to 3.0
0 to 0.050
Iron (Fe), % 0 to 1.3
0 to 0.19
Magnesium (Mg), % 0 to 0.1
0.25 to 0.45
Manganese (Mn), % 0 to 0.5
0 to 0.1
Nickel (Ni), % 0 to 0.3
0
Silicon (Si), % 9.5 to 11.5
9.0 to 10
Tin (Sn), % 0 to 0.15
0
Titanium (Ti), % 0
0 to 0.15
Zinc (Zn), % 0 to 3.0
0 to 0.070
Residuals, % 0 to 0.5
0 to 0.1