384.0 Aluminum vs. AWS ERNiCrMo-10

384.0 aluminum belongs to the aluminum alloys classification, while AWS ERNiCrMo-10 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 384.0 aluminum and the bottom bar is AWS ERNiCrMo-10.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 74
220
Elongation at Break, % 2.5
28
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 28
84
Tensile Strength: Ultimate (UTS), MPa 330
790

Thermal Properties

Latent Heat of Fusion, J/g 550
320
Melting Completion (Liquidus), °C 580
1550
Melting Onset (Solidus), °C 530
1490
Specific Heat Capacity, J/kg-K 870
420
Thermal Conductivity, W/m-K 96
10
Thermal Expansion, µm/m-K 21
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 69
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 11
70
Density, g/cm3 2.9
8.9
Embodied Carbon, kg CO2/kg material 7.4
12
Embodied Energy, MJ/kg 140
160
Embodied Water, L/kg 1010
300

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 49
23
Strength to Weight: Axial, points 32
25
Strength to Weight: Bending, points 37
21
Thermal Diffusivity, mm2/s 39
2.7
Thermal Shock Resistance, points 15
21

Alloy Composition

Aluminum (Al), % 77.3 to 86.5
0
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
20 to 22.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 3.0 to 4.5
0 to 0.5
Iron (Fe), % 0 to 1.3
2.0 to 6.0
Magnesium (Mg), % 0 to 0.1
0
Manganese (Mn), % 0 to 0.5
0 to 0.5
Molybdenum (Mo), % 0
12.5 to 14.5
Nickel (Ni), % 0 to 0.5
49 to 63
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 10.5 to 12
0 to 0.080
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 0 to 0.35
0
Tungsten (W), % 0
2.5 to 3.5
Vanadium (V), % 0
0 to 0.35
Zinc (Zn), % 0 to 3.0
0
Residuals, % 0
0 to 0.5