384.0 Aluminum vs. EN-MC21310 Magnesium
384.0 aluminum belongs to the aluminum alloys classification, while EN-MC21310 magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 384.0 aluminum and the bottom bar is EN-MC21310 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 85 | |
| 60 |
| Elastic (Young's, Tensile) Modulus, GPa | 74 | |
| 45 |
| Elongation at Break, % | 2.5 | |
| 9.0 |
| Fatigue Strength, MPa | 140 | |
| 86 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 28 | |
| 17 |
| Shear Strength, MPa | 200 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 330 | |
| 200 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 550 | |
| 360 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 100 |
| Melting Completion (Liquidus), °C | 580 | |
| 600 |
| Melting Onset (Solidus), °C | 530 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 1000 |
| Thermal Conductivity, W/m-K | 96 | |
| 89 |
| Thermal Expansion, µm/m-K | 21 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 22 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 69 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 12 |
| Density, g/cm3 | 2.9 | |
| 1.6 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 23 |
| Embodied Energy, MJ/kg | 140 | |
| 160 |
| Embodied Water, L/kg | 1010 | |
| 970 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.9 | |
| 16 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 | |
| 160 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 49 | |
| 73 |
| Strength to Weight: Axial, points | 32 | |
| 34 |
| Strength to Weight: Bending, points | 37 | |
| 47 |
| Thermal Diffusivity, mm2/s | 39 | |
| 55 |
| Thermal Shock Resistance, points | 15 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 77.3 to 86.5 | |
| 1.8 to 2.6 |
| Copper (Cu), % | 3.0 to 4.5 | |
| 0 to 0.010 |
| Iron (Fe), % | 0 to 1.3 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0 to 0.1 | |
| 95.2 to 97.4 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.1 to 0.7 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 to 0.0020 |
| Silicon (Si), % | 10.5 to 12 | |
| 0.7 to 1.2 |
| Tin (Sn), % | 0 to 0.35 | |
| 0 |
| Zinc (Zn), % | 0 to 3.0 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.010 |