384.0 Aluminum vs. R30006 Cobalt

384.0 aluminum belongs to the aluminum alloys classification, while R30006 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 384.0 aluminum and the bottom bar is R30006 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 74
220
Elongation at Break, % 2.5
1.0
Fatigue Strength, MPa 140
260
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 28
85
Tensile Strength: Ultimate (UTS), MPa 330
900
Tensile Strength: Yield (Proof), MPa 170
540

Thermal Properties

Latent Heat of Fusion, J/g 550
320
Melting Completion (Liquidus), °C 580
1400
Melting Onset (Solidus), °C 530
1290
Specific Heat Capacity, J/kg-K 870
450
Thermal Conductivity, W/m-K 96
15
Thermal Expansion, µm/m-K 21
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 69
1.7

Otherwise Unclassified Properties

Density, g/cm3 2.9
8.6
Embodied Carbon, kg CO2/kg material 7.4
7.8
Embodied Energy, MJ/kg 140
110
Embodied Water, L/kg 1010
500

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.9
7.8
Resilience: Unit (Modulus of Resilience), kJ/m3 190
670
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 49
23
Strength to Weight: Axial, points 32
29
Strength to Weight: Bending, points 37
24
Thermal Diffusivity, mm2/s 39
3.9
Thermal Shock Resistance, points 15
26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 77.3 to 86.5
0
Carbon (C), % 0
0.9 to 1.4
Chromium (Cr), % 0
27 to 32
Cobalt (Co), % 0
48.6 to 68.1
Copper (Cu), % 3.0 to 4.5
0
Iron (Fe), % 0 to 1.3
0 to 3.0
Magnesium (Mg), % 0 to 0.1
0
Manganese (Mn), % 0 to 0.5
0
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 0 to 0.5
0 to 3.0
Silicon (Si), % 10.5 to 12
0 to 2.0
Tin (Sn), % 0 to 0.35
0
Tungsten (W), % 0
4.0 to 6.0
Zinc (Zn), % 0 to 3.0
0
Residuals, % 0 to 0.5
0