384.0 Aluminum vs. Z21210 Zinc

384.0 aluminum belongs to the aluminum alloys classification, while Z21210 zinc belongs to the zinc alloys. There are 12 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 384.0 aluminum and the bottom bar is Z21210 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Tensile Strength: Ultimate (UTS), MPa 330
150 to 170

Thermal Properties

Melting Completion (Liquidus), °C 580
Melting Onset (Solidus), °C 530
Specific Heat Capacity, J/kg-K 870
Thermal Conductivity, W/m-K 96
Thermal Expansion, µm/m-K 21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
Electrical Conductivity: Equal Weight (Specific), % IACS 69

Otherwise Unclassified Properties

Density, g/cm3 2.9

Common Calculations

Strength to Weight: Axial, points 32
5.7 to 6.4
Strength to Weight: Bending, points 37
8.6 to 9.4
Thermal Diffusivity, mm2/s 39