390.0 Aluminum vs. 444.0 Aluminum

Both 390.0 aluminum and 444.0 aluminum are aluminum alloys. They have 85% of their average alloy composition in common.

For each property being compared, the top bar is 390.0 aluminum and the bottom bar is 444.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
50
Elastic (Young's, Tensile) Modulus, GPa 75
71
Elongation at Break, % 1.0
25
Fatigue Strength, MPa 76 to 110
51
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 28
27
Tensile Strength: Ultimate (UTS), MPa 280 to 300
190
Tensile Strength: Yield (Proof), MPa 240 to 270
83

Thermal Properties

Latent Heat of Fusion, J/g 640
500
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 650
610
Melting Onset (Solidus), °C 560
600
Specific Heat Capacity, J/kg-K 880
900
Thermal Conductivity, W/m-K 130
160
Thermal Expansion, µm/m-K 18
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24 to 25
40
Electrical Conductivity: Equal Weight (Specific), % IACS 79 to 83
140

Otherwise Unclassified Properties

Base Metal Price, % relative 11
9.5
Density, g/cm3 2.7
2.6
Embodied Carbon, kg CO2/kg material 7.3
7.9
Embodied Energy, MJ/kg 130
150
Embodied Water, L/kg 950
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.7 to 2.9
39
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 470
49
Stiffness to Weight: Axial, points 15
15
Stiffness to Weight: Bending, points 52
53
Strength to Weight: Axial, points 28 to 30
20
Strength to Weight: Bending, points 35 to 36
28
Thermal Diffusivity, mm2/s 56
67
Thermal Shock Resistance, points 14 to 15
8.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 74.5 to 79.6
90.5 to 93.5
Copper (Cu), % 4.0 to 5.0
0 to 0.25
Iron (Fe), % 0 to 1.3
0 to 0.6
Magnesium (Mg), % 0.45 to 0.65
0 to 0.1
Manganese (Mn), % 0 to 0.1
0 to 0.35
Silicon (Si), % 16 to 18
6.5 to 7.5
Titanium (Ti), % 0 to 0.2
0 to 0.25
Zinc (Zn), % 0 to 0.1
0 to 0.35
Residuals, % 0 to 0.2
0 to 0.15