390.0 Aluminum vs. EN AC-42000 Aluminum

Both 390.0 aluminum and EN AC-42000 aluminum are aluminum alloys. They have 85% of their average alloy composition in common.

For each property being compared, the top bar is 390.0 aluminum and the bottom bar is EN AC-42000 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
59 to 91
Elastic (Young's, Tensile) Modulus, GPa 75
70
Elongation at Break, % 1.0
1.1 to 2.4
Fatigue Strength, MPa 76 to 110
67 to 76
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 28
26
Tensile Strength: Ultimate (UTS), MPa 280 to 300
170 to 270
Tensile Strength: Yield (Proof), MPa 240 to 270
95 to 230

Thermal Properties

Latent Heat of Fusion, J/g 640
500
Maximum Temperature: Mechanical, °C 170
170
Melting Completion (Liquidus), °C 650
610
Melting Onset (Solidus), °C 560
600
Specific Heat Capacity, J/kg-K 880
900
Thermal Conductivity, W/m-K 130
160
Thermal Expansion, µm/m-K 18
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24 to 25
38
Electrical Conductivity: Equal Weight (Specific), % IACS 79 to 83
130

Otherwise Unclassified Properties

Base Metal Price, % relative 11
9.5
Density, g/cm3 2.7
2.6
Embodied Carbon, kg CO2/kg material 7.3
8.0
Embodied Energy, MJ/kg 130
150
Embodied Water, L/kg 950
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.7 to 2.9
2.8 to 5.7
Resilience: Unit (Modulus of Resilience), kJ/m3 380 to 470
64 to 370
Stiffness to Weight: Axial, points 15
15
Stiffness to Weight: Bending, points 52
53
Strength to Weight: Axial, points 28 to 30
18 to 28
Strength to Weight: Bending, points 35 to 36
26 to 35
Thermal Diffusivity, mm2/s 56
66
Thermal Shock Resistance, points 14 to 15
7.9 to 12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 74.5 to 79.6
89.9 to 93.3
Copper (Cu), % 4.0 to 5.0
0 to 0.2
Iron (Fe), % 0 to 1.3
0 to 0.55
Lead (Pb), % 0
0 to 0.15
Magnesium (Mg), % 0.45 to 0.65
0.2 to 0.65
Manganese (Mn), % 0 to 0.1
0 to 0.35
Nickel (Ni), % 0
0 to 0.15
Silicon (Si), % 16 to 18
6.5 to 7.5
Tin (Sn), % 0
0 to 0.050
Titanium (Ti), % 0 to 0.2
0 to 0.25
Zinc (Zn), % 0 to 0.1
0 to 0.15
Residuals, % 0 to 0.2
0 to 0.15

Comparable Variants