4004 Aluminum vs. 710.0 Aluminum

Both 4004 aluminum and 710.0 aluminum are aluminum alloys. They have 89% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is 4004 aluminum and the bottom bar is 710.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
70
Elongation at Break, % 2.4
2.2 to 3.6
Fatigue Strength, MPa 42
55 to 110
Poisson's Ratio 0.33
0.32
Shear Modulus, GPa 27
26
Shear Strength, MPa 63
180
Tensile Strength: Ultimate (UTS), MPa 110
240 to 250
Tensile Strength: Yield (Proof), MPa 60
160

Thermal Properties

Latent Heat of Fusion, J/g 540
380
Maximum Temperature: Mechanical, °C 160
170
Melting Completion (Liquidus), °C 600
650
Melting Onset (Solidus), °C 560
610
Specific Heat Capacity, J/kg-K 910
870
Thermal Conductivity, W/m-K 130
140
Thermal Expansion, µm/m-K 22
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 33
35
Electrical Conductivity: Equal Weight (Specific), % IACS 120
110

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.6
3.0
Embodied Carbon, kg CO2/kg material 8.0
8.0
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1070
1130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.3
4.9 to 7.9
Resilience: Unit (Modulus of Resilience), kJ/m3 25
180 to 190
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 54
46
Strength to Weight: Axial, points 12
23
Strength to Weight: Bending, points 20
29
Thermal Diffusivity, mm2/s 58
53
Thermal Shock Resistance, points 5.1
10 to 11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 86 to 90
90.5 to 93.1
Copper (Cu), % 0 to 0.25
0.35 to 0.65
Iron (Fe), % 0 to 0.8
0 to 0.5
Magnesium (Mg), % 1.0 to 2.0
0.6 to 0.8
Manganese (Mn), % 0 to 0.1
0 to 0.050
Silicon (Si), % 9.0 to 10.5
0 to 0.15
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0 to 0.2
6.0 to 7.0
Residuals, % 0 to 0.15
0 to 0.15