4145 Aluminum vs. EN 1.5701 Steel

4145 aluminum belongs to the aluminum alloys classification, while EN 1.5701 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 4145 aluminum and the bottom bar is EN 1.5701 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 73
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 28
73
Tensile Strength: Ultimate (UTS), MPa 120
430 to 1300

Thermal Properties

Latent Heat of Fusion, J/g 540
250
Maximum Temperature: Mechanical, °C 160
410
Melting Completion (Liquidus), °C 590
1460
Melting Onset (Solidus), °C 520
1420
Specific Heat Capacity, J/kg-K 880
470
Thermal Conductivity, W/m-K 100
45
Thermal Expansion, µm/m-K 21
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 84
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.4
Density, g/cm3 2.8
7.9
Embodied Carbon, kg CO2/kg material 7.6
1.5
Embodied Energy, MJ/kg 140
19
Embodied Water, L/kg 1040
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 12
15 to 46
Strength to Weight: Bending, points 19
16 to 34
Thermal Diffusivity, mm2/s 42
12
Thermal Shock Resistance, points 5.5
13 to 38

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 83 to 87.4
0
Carbon (C), % 0
0.090 to 0.15
Chromium (Cr), % 0 to 0.15
0.4 to 0.7
Copper (Cu), % 3.3 to 4.7
0 to 0.25
Iron (Fe), % 0 to 0.8
97.2 to 98.7
Magnesium (Mg), % 0 to 0.15
0
Manganese (Mn), % 0 to 0.15
0.3 to 0.6
Nickel (Ni), % 0
0.5 to 0.8
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 9.3 to 10.7
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.15
0