4145 Aluminum vs. EN 1.7076 Steel

4145 aluminum belongs to the aluminum alloys classification, while EN 1.7076 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 4145 aluminum and the bottom bar is EN 1.7076 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 73
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 28
73
Tensile Strength: Ultimate (UTS), MPa 120
470 to 1700

Thermal Properties

Latent Heat of Fusion, J/g 540
250
Maximum Temperature: Mechanical, °C 160
420
Melting Completion (Liquidus), °C 590
1460
Melting Onset (Solidus), °C 520
1420
Specific Heat Capacity, J/kg-K 880
470
Thermal Conductivity, W/m-K 100
45
Thermal Expansion, µm/m-K 21
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 84
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.3
Density, g/cm3 2.8
7.8
Embodied Carbon, kg CO2/kg material 7.6
1.4
Embodied Energy, MJ/kg 140
19
Embodied Water, L/kg 1040
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 12
17 to 60
Strength to Weight: Bending, points 19
17 to 40
Thermal Diffusivity, mm2/s 42
12
Thermal Shock Resistance, points 5.5
14 to 50

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 83 to 87.4
0
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0
0.3 to 0.34
Chromium (Cr), % 0 to 0.15
0.9 to 1.2
Copper (Cu), % 3.3 to 4.7
0 to 0.25
Iron (Fe), % 0 to 0.8
97 to 98.2
Magnesium (Mg), % 0 to 0.15
0
Manganese (Mn), % 0 to 0.15
0.6 to 0.9
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 9.3 to 10.7
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.15
0