5005 Aluminum vs. 5005-O Aluminum
5005-O aluminum is a variant of 5005 aluminum. The properties of the parent material encompass the values of all of its variants.
For each property being compared, the top bar is 5005 aluminum and the bottom bar is 5005-O aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 28 to 64 | |
| 28 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 1.1 to 23 | |
| 23 |
| Fatigue Strength, MPa | 38 to 86 | |
| 45 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 70 to 130 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 110 to 230 | |
| 120 |
| Tensile Strength: Yield (Proof), MPa | 41 to 210 | |
| 41 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 630 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 200 | |
| 200 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 52 | |
| 52 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 170 | |
| 170 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Calomel Potential, mV | -740 | |
| -740 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.3 to 22 | |
| 22 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 12 to 320 | |
| 12 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 11 to 23 | |
| 12 |
| Strength to Weight: Bending, points | 19 to 31 | |
| 20 |
| Thermal Diffusivity, mm2/s | 82 | |
| 82 |
| Thermal Shock Resistance, points | 4.9 to 10 | |
| 5.4 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97 to 99.5 | |
| 97 to 99.5 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0.5 to 1.1 | |
| 0.5 to 1.1 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.3 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.25 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |