5005-H38 Aluminum vs. 5457-H38 Aluminum
Both 5005-H38 aluminum and 5457-H38 aluminum are aluminum alloys. Both are furnished in the H38 temper. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 5005-H38 aluminum and the bottom bar is 5457-H38 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 53 | |
| 55 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 3.8 | |
| 6.0 |
| Fatigue Strength, MPa | 84 | |
| 89 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 110 | |
| 130 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 180 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 650 | |
| 660 |
| Melting Onset (Solidus), °C | 630 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 200 | |
| 180 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 52 | |
| 46 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 170 | |
| 150 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.4 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1190 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.4 | |
| 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
| 250 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 21 | |
| 21 |
| Strength to Weight: Bending, points | 28 | |
| 28 |
| Thermal Diffusivity, mm2/s | 82 | |
| 72 |
| Thermal Shock Resistance, points | 8.9 | |
| 9.0 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97 to 99.5 | |
| 97.8 to 99.05 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 0.5 to 1.1 | |
| 0.8 to 1.2 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0.15 to 0.45 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.080 |
| Vanadium (V), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.050 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.1 |