5005A Aluminum vs. 3303 Aluminum

Both 5005A aluminum and 3303 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is 5005A aluminum and the bottom bar is 3303 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
70
Elongation at Break, % 1.1 to 21
23
Fatigue Strength, MPa 38 to 82
43
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
26
Shear Strength, MPa 71 to 130
69
Tensile Strength: Ultimate (UTS), MPa 110 to 230
110
Tensile Strength: Yield (Proof), MPa 43 to 210
39

Thermal Properties

Latent Heat of Fusion, J/g 400
400
Maximum Temperature: Mechanical, °C 180
180
Melting Completion (Liquidus), °C 660
650
Melting Onset (Solidus), °C 630
620
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 200
170
Thermal Expansion, µm/m-K 24
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 52
43
Electrical Conductivity: Equal Weight (Specific), % IACS 170
140

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.8
Embodied Carbon, kg CO2/kg material 8.3
8.1
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1190
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.0 to 19
20
Resilience: Unit (Modulus of Resilience), kJ/m3 14 to 310
11
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
49
Strength to Weight: Axial, points 12 to 24
11
Strength to Weight: Bending, points 19 to 31
18
Thermal Diffusivity, mm2/s 82
67
Thermal Shock Resistance, points 5.0 to 10
4.8

Alloy Composition

Aluminum (Al), % 97.5 to 99.3
96.6 to 99
Chromium (Cr), % 0 to 0.1
0
Copper (Cu), % 0 to 0.050
0.050 to 0.2
Iron (Fe), % 0 to 0.45
0 to 0.7
Magnesium (Mg), % 0.7 to 1.1
0
Manganese (Mn), % 0 to 0.15
1.0 to 1.5
Silicon (Si), % 0 to 0.3
0 to 0.6
Zinc (Zn), % 0 to 0.2
0 to 0.3
Residuals, % 0
0 to 0.15