5019 Aluminum vs. C43000 Brass
5019 aluminum belongs to the aluminum alloys classification, while C43000 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5019 aluminum and the bottom bar is C43000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 110 |
| Elongation at Break, % | 2.2 to 18 | |
| 3.0 to 55 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 42 |
| Shear Strength, MPa | 170 to 210 | |
| 230 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 360 | |
| 320 to 710 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 130 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 1030 |
| Melting Onset (Solidus), °C | 540 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 380 |
| Thermal Conductivity, W/m-K | 130 | |
| 120 |
| Thermal Expansion, µm/m-K | 24 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 98 | |
| 28 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 29 |
| Density, g/cm3 | 2.7 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 9.0 | |
| 2.8 |
| Embodied Energy, MJ/kg | 150 | |
| 46 |
| Embodied Water, L/kg | 1180 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.6 to 40 | |
| 20 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 650 | |
| 82 to 1350 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 51 | |
| 19 |
| Strength to Weight: Axial, points | 29 to 38 | |
| 10 to 23 |
| Strength to Weight: Bending, points | 35 to 42 | |
| 12 to 20 |
| Thermal Diffusivity, mm2/s | 52 | |
| 36 |
| Thermal Shock Resistance, points | 13 to 16 | |
| 11 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 91.5 to 95.3 | |
| 0 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 0 to 0.1 | |
| 84 to 87 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 4.5 to 5.6 | |
| 0 |
| Manganese (Mn), % | 0.1 to 0.6 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.7 to 2.7 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 9.7 to 14.3 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.5 |