5019 Aluminum vs. Zamak 3

5019 aluminum belongs to the aluminum alloys classification, while Zamak 3 belongs to the zinc alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5019 aluminum and the bottom bar is Zamak 3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
86
Elongation at Break, % 2.2 to 18
11
Fatigue Strength, MPa 100 to 160
48
Poisson's Ratio 0.33
0.25
Shear Modulus, GPa 26
33
Shear Strength, MPa 170 to 210
210
Tensile Strength: Ultimate (UTS), MPa 280 to 360
280
Tensile Strength: Yield (Proof), MPa 120 to 300
210

Thermal Properties

Latent Heat of Fusion, J/g 400
120
Maximum Temperature: Mechanical, °C 180
95
Melting Completion (Liquidus), °C 640
390
Melting Onset (Solidus), °C 540
380
Specific Heat Capacity, J/kg-K 900
410
Thermal Conductivity, W/m-K 130
110
Thermal Expansion, µm/m-K 24
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 29
27
Electrical Conductivity: Equal Weight (Specific), % IACS 98
38

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
11
Density, g/cm3 2.7
6.4
Embodied Carbon, kg CO2/kg material 9.0
3.0
Embodied Energy, MJ/kg 150
57
Embodied Water, L/kg 1180
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 7.6 to 40
28
Resilience: Unit (Modulus of Resilience), kJ/m3 110 to 650
260
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 51
23
Strength to Weight: Axial, points 29 to 38
12
Strength to Weight: Bending, points 35 to 42
15
Thermal Diffusivity, mm2/s 52
43
Thermal Shock Resistance, points 13 to 16
8.6

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 91.5 to 95.3
3.5 to 4.3
Cadmium (Cd), % 0
0 to 0.0050
Chromium (Cr), % 0 to 0.2
0
Copper (Cu), % 0 to 0.1
0 to 0.25
Iron (Fe), % 0 to 0.5
0 to 0.1
Lead (Pb), % 0
0 to 0.0050
Magnesium (Mg), % 4.5 to 5.6
0.020 to 0.060
Manganese (Mn), % 0.1 to 0.6
0
Nickel (Ni), % 0
0 to 0.020
Silicon (Si), % 0 to 0.4
0 to 0.030
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.2
95.3 to 96.5
Residuals, % 0 to 0.15
0