5019 Aluminum vs. ZA-12

5019 aluminum belongs to the aluminum alloys classification, while ZA-12 belongs to the zinc alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5019 aluminum and the bottom bar is ZA-12.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
83
Elongation at Break, % 2.2 to 18
1.6 to 5.3
Fatigue Strength, MPa 100 to 160
73 to 120
Poisson's Ratio 0.33
0.26
Shear Modulus, GPa 26
33
Shear Strength, MPa 170 to 210
240 to 300
Tensile Strength: Ultimate (UTS), MPa 280 to 360
260 to 400
Tensile Strength: Yield (Proof), MPa 120 to 300
210 to 320

Thermal Properties

Latent Heat of Fusion, J/g 400
120
Maximum Temperature: Mechanical, °C 180
100
Melting Completion (Liquidus), °C 640
430
Melting Onset (Solidus), °C 540
380
Specific Heat Capacity, J/kg-K 900
450
Thermal Conductivity, W/m-K 130
120
Thermal Expansion, µm/m-K 24
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 29
28
Electrical Conductivity: Equal Weight (Specific), % IACS 98
42

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
11
Density, g/cm3 2.7
6.0
Embodied Carbon, kg CO2/kg material 9.0
3.4
Embodied Energy, MJ/kg 150
64
Embodied Water, L/kg 1180
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 7.6 to 40
4.0 to 20
Resilience: Unit (Modulus of Resilience), kJ/m3 110 to 650
260 to 620
Stiffness to Weight: Axial, points 14
7.6
Stiffness to Weight: Bending, points 51
24
Strength to Weight: Axial, points 29 to 38
12 to 19
Strength to Weight: Bending, points 35 to 42
15 to 20
Thermal Diffusivity, mm2/s 52
43
Thermal Shock Resistance, points 13 to 16
9.4 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 91.5 to 95.3
10.5 to 11.5
Cadmium (Cd), % 0
0 to 0.0060
Chromium (Cr), % 0 to 0.2
0
Copper (Cu), % 0 to 0.1
0.5 to 1.2
Iron (Fe), % 0 to 0.5
0 to 0.075
Lead (Pb), % 0
0 to 0.0060
Magnesium (Mg), % 4.5 to 5.6
0.015 to 0.030
Manganese (Mn), % 0.1 to 0.6
0
Nickel (Ni), % 0
0 to 0.020
Silicon (Si), % 0 to 0.4
0 to 0.060
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.2
87.1 to 89
Residuals, % 0 to 0.15
0