5026 Aluminum vs. 6261 Aluminum
Both 5026 aluminum and 6261 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common.
For each property being compared, the top bar is 5026 aluminum and the bottom bar is 6261 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 69 |
| Elongation at Break, % | 5.1 to 11 | |
| 9.0 to 16 |
| Fatigue Strength, MPa | 94 to 140 | |
| 60 to 120 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 150 to 180 | |
| 90 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 320 | |
| 150 to 300 |
| Tensile Strength: Yield (Proof), MPa | 120 to 250 | |
| 100 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 160 |
| Melting Completion (Liquidus), °C | 650 | |
| 640 |
| Melting Onset (Solidus), °C | 510 | |
| 610 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 180 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 31 | |
| 48 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 99 | |
| 160 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.8 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1150 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 to 29 | |
| 21 to 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 440 | |
| 77 to 500 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 49 | |
| 50 |
| Strength to Weight: Axial, points | 26 to 32 | |
| 15 to 31 |
| Strength to Weight: Bending, points | 33 to 37 | |
| 23 to 37 |
| Thermal Diffusivity, mm2/s | 52 | |
| 75 |
| Thermal Shock Resistance, points | 11 to 14 | |
| 6.5 to 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 88.2 to 94.7 | |
| 96.6 to 98.6 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 to 0.1 |
| Copper (Cu), % | 0.1 to 0.8 | |
| 0.15 to 0.4 |
| Iron (Fe), % | 0.2 to 1.0 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 3.9 to 4.9 | |
| 0.7 to 1.0 |
| Manganese (Mn), % | 0.6 to 1.8 | |
| 0.2 to 0.35 |
| Silicon (Si), % | 0.55 to 1.4 | |
| 0.4 to 0.7 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 to 0.2 |
| Zirconium (Zr), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |