5070 Aluminum vs. A390.0 Aluminum

Both 5070 aluminum and A390.0 aluminum are aluminum alloys. They have 79% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is A390.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
75
Elongation at Break, % 20
0.87 to 0.91
Fatigue Strength, MPa 150
70 to 100
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
28
Tensile Strength: Ultimate (UTS), MPa 300
190 to 290
Tensile Strength: Yield (Proof), MPa 140
190 to 290

Thermal Properties

Latent Heat of Fusion, J/g 390
640
Maximum Temperature: Mechanical, °C 190
170
Melting Completion (Liquidus), °C 640
580
Melting Onset (Solidus), °C 550
480
Specific Heat Capacity, J/kg-K 900
880
Thermal Conductivity, W/m-K 130
130
Thermal Expansion, µm/m-K 24
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
20
Electrical Conductivity: Equal Weight (Specific), % IACS 100
67

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
11
Density, g/cm3 2.7
2.7
Embodied Carbon, kg CO2/kg material 8.8
7.3
Embodied Energy, MJ/kg 150
140
Embodied Water, L/kg 1170
950

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 51
1.6 to 2.6
Resilience: Unit (Modulus of Resilience), kJ/m3 150
240 to 580
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 50
52
Strength to Weight: Axial, points 31
19 to 30
Strength to Weight: Bending, points 37
27 to 36
Thermal Diffusivity, mm2/s 53
56
Thermal Shock Resistance, points 14
9.0 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
75.3 to 79.6
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.25
4.0 to 5.0
Iron (Fe), % 0 to 0.4
0 to 0.5
Magnesium (Mg), % 3.5 to 4.5
0.45 to 0.65
Manganese (Mn), % 0.4 to 0.8
0 to 0.1
Silicon (Si), % 0 to 0.25
16 to 18
Titanium (Ti), % 0 to 0.15
0 to 0.2
Zinc (Zn), % 0.4 to 0.8
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.2