5070 Aluminum vs. AWS E3155

5070 aluminum belongs to the aluminum alloys classification, while AWS E3155 belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is AWS E3155.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
210
Elongation at Break, % 20
23
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
81
Tensile Strength: Ultimate (UTS), MPa 300
770

Thermal Properties

Latent Heat of Fusion, J/g 390
310
Melting Completion (Liquidus), °C 640
1460
Melting Onset (Solidus), °C 550
1410
Specific Heat Capacity, J/kg-K 900
450
Thermal Conductivity, W/m-K 130
13
Thermal Expansion, µm/m-K 24
13

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
70
Density, g/cm3 2.7
8.4
Embodied Carbon, kg CO2/kg material 8.8
7.7
Embodied Energy, MJ/kg 150
110
Embodied Water, L/kg 1170
300

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 31
26
Strength to Weight: Bending, points 37
22
Thermal Diffusivity, mm2/s 53
3.3
Thermal Shock Resistance, points 14
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
0
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0 to 0.3
20 to 22.5
Cobalt (Co), % 0
18.5 to 21
Copper (Cu), % 0 to 0.25
0 to 0.75
Iron (Fe), % 0 to 0.4
23.3 to 36.3
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0.4 to 0.8
1.0 to 2.5
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0
19 to 21
Niobium (Nb), % 0
0.75 to 1.3
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.25
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0 to 0.15
0
Tungsten (W), % 0
2.0 to 3.0
Zinc (Zn), % 0.4 to 0.8
0
Residuals, % 0 to 0.15
0