5070 Aluminum vs. AWS ERTi-12

5070 aluminum belongs to the aluminum alloys classification, while AWS ERTi-12 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is AWS ERTi-12.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
110
Elongation at Break, % 20
12
Fatigue Strength, MPa 150
200
Poisson's Ratio 0.33
0.32
Shear Modulus, GPa 26
41
Tensile Strength: Ultimate (UTS), MPa 300
480
Tensile Strength: Yield (Proof), MPa 140
340

Thermal Properties

Latent Heat of Fusion, J/g 390
420
Maximum Temperature: Mechanical, °C 190
320
Melting Completion (Liquidus), °C 640
1670
Melting Onset (Solidus), °C 550
1620
Specific Heat Capacity, J/kg-K 900
540
Thermal Conductivity, W/m-K 130
21
Thermal Expansion, µm/m-K 24
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 100
7.1

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
37
Density, g/cm3 2.7
4.5
Embodied Carbon, kg CO2/kg material 8.8
31
Embodied Energy, MJ/kg 150
510
Embodied Water, L/kg 1170
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 51
52
Resilience: Unit (Modulus of Resilience), kJ/m3 150
550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
35
Strength to Weight: Axial, points 31
30
Strength to Weight: Bending, points 37
30
Thermal Diffusivity, mm2/s 53
8.7
Thermal Shock Resistance, points 14
37

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.25
0
Hydrogen (H), % 0
0 to 0.0080
Iron (Fe), % 0 to 0.4
0 to 0.15
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0.4 to 0.8
0
Molybdenum (Mo), % 0
0.2 to 0.4
Nickel (Ni), % 0
0.060 to 0.090
Nitrogen (N), % 0
0 to 0.015
Oxygen (O), % 0
0.080 to 0.16
Silicon (Si), % 0 to 0.25
0
Titanium (Ti), % 0 to 0.15
99.147 to 99.66
Zinc (Zn), % 0.4 to 0.8
0
Residuals, % 0 to 0.15
0