5070 Aluminum vs. EN 1.0033 Steel

5070 aluminum belongs to the aluminum alloys classification, while EN 1.0033 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is EN 1.0033 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
190
Elongation at Break, % 20
17 to 32
Fatigue Strength, MPa 150
120 to 140
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
73
Shear Strength, MPa 190
200
Tensile Strength: Ultimate (UTS), MPa 300
300 to 330
Tensile Strength: Yield (Proof), MPa 140
150 to 200

Thermal Properties

Latent Heat of Fusion, J/g 390
250
Maximum Temperature: Mechanical, °C 190
400
Melting Completion (Liquidus), °C 640
1470
Melting Onset (Solidus), °C 550
1420
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 130
53
Thermal Expansion, µm/m-K 24
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 100
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
1.8
Density, g/cm3 2.7
7.9
Embodied Carbon, kg CO2/kg material 8.8
1.4
Embodied Energy, MJ/kg 150
18
Embodied Water, L/kg 1170
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 51
48 to 83
Resilience: Unit (Modulus of Resilience), kJ/m3 150
63 to 100
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 31
10 to 12
Strength to Weight: Bending, points 37
13 to 14
Thermal Diffusivity, mm2/s 53
14
Thermal Shock Resistance, points 14
9.4 to 10

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
0
Carbon (C), % 0
0 to 0.11
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 0 to 0.4
98.8 to 100
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0.4 to 0.8
0 to 0.7
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.25
0 to 0.35
Sulfur (S), % 0
0 to 0.045
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0.4 to 0.8
0
Residuals, % 0 to 0.15
0