5070 Aluminum vs. EN 1.8875 Steel

5070 aluminum belongs to the aluminum alloys classification, while EN 1.8875 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is EN 1.8875 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
190
Elongation at Break, % 20
19
Fatigue Strength, MPa 150
340
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
73
Shear Strength, MPa 190
410
Tensile Strength: Ultimate (UTS), MPa 300
660
Tensile Strength: Yield (Proof), MPa 140
490

Thermal Properties

Latent Heat of Fusion, J/g 390
250
Maximum Temperature: Mechanical, °C 190
420
Melting Completion (Liquidus), °C 640
1460
Melting Onset (Solidus), °C 550
1420
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 130
39
Thermal Expansion, µm/m-K 24
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 100
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
3.2
Density, g/cm3 2.7
7.9
Embodied Carbon, kg CO2/kg material 8.8
1.8
Embodied Energy, MJ/kg 150
24
Embodied Water, L/kg 1170
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 51
110
Resilience: Unit (Modulus of Resilience), kJ/m3 150
650
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 31
23
Strength to Weight: Bending, points 37
21
Thermal Diffusivity, mm2/s 53
10
Thermal Shock Resistance, points 14
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
0
Boron (B), % 0
0 to 0.0050
Carbon (C), % 0
0 to 0.18
Chromium (Cr), % 0 to 0.3
0 to 1.0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 0 to 0.4
93.6 to 100
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0.4 to 0.8
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.7
Nickel (Ni), % 0
0 to 1.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0 to 0.25
0 to 0.6
Sulfur (S), % 0
0 to 0.0080
Titanium (Ti), % 0 to 0.15
0 to 0.050
Vanadium (V), % 0
0 to 0.080
Zinc (Zn), % 0.4 to 0.8
0
Zirconium (Zr), % 0
0 to 0.15
Residuals, % 0 to 0.15
0