5070 Aluminum vs. EN AC-44200 Aluminum

Both 5070 aluminum and EN AC-44200 aluminum are aluminum alloys. They have 88% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is EN AC-44200 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
72
Elongation at Break, % 20
6.2
Fatigue Strength, MPa 150
63
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
27
Tensile Strength: Ultimate (UTS), MPa 300
180
Tensile Strength: Yield (Proof), MPa 140
86

Thermal Properties

Latent Heat of Fusion, J/g 390
570
Maximum Temperature: Mechanical, °C 190
170
Melting Completion (Liquidus), °C 640
590
Melting Onset (Solidus), °C 550
580
Specific Heat Capacity, J/kg-K 900
910
Thermal Conductivity, W/m-K 130
130
Thermal Expansion, µm/m-K 24
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
35
Electrical Conductivity: Equal Weight (Specific), % IACS 100
130

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.5
Embodied Carbon, kg CO2/kg material 8.8
7.7
Embodied Energy, MJ/kg 150
140
Embodied Water, L/kg 1170
1050

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 51
9.1
Resilience: Unit (Modulus of Resilience), kJ/m3 150
51
Stiffness to Weight: Axial, points 14
16
Stiffness to Weight: Bending, points 50
55
Strength to Weight: Axial, points 31
20
Strength to Weight: Bending, points 37
28
Thermal Diffusivity, mm2/s 53
59
Thermal Shock Resistance, points 14
8.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
85.2 to 89.5
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.25
0 to 0.050
Iron (Fe), % 0 to 0.4
0 to 0.55
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0.4 to 0.8
0 to 0.35
Silicon (Si), % 0 to 0.25
10.5 to 13.5
Titanium (Ti), % 0 to 0.15
0 to 0.15
Zinc (Zn), % 0.4 to 0.8
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15