5070 Aluminum vs. Low-oxygen Zirconium

5070 aluminum belongs to the aluminum alloys classification, while low-oxygen zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is low-oxygen zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
98
Elongation at Break, % 20
23
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
37
Tensile Strength: Ultimate (UTS), MPa 300
330
Tensile Strength: Yield (Proof), MPa 140
270

Thermal Properties

Latent Heat of Fusion, J/g 390
250
Specific Heat Capacity, J/kg-K 900
270
Thermal Conductivity, W/m-K 130
22
Thermal Expansion, µm/m-K 24
5.7

Otherwise Unclassified Properties

Density, g/cm3 2.7
6.7
Embodied Water, L/kg 1170
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 51
70
Resilience: Unit (Modulus of Resilience), kJ/m3 150
370
Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 50
23
Strength to Weight: Axial, points 31
14
Strength to Weight: Bending, points 37
16
Thermal Diffusivity, mm2/s 53
12
Thermal Shock Resistance, points 14
42

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0 to 0.3
0 to 0.2
Copper (Cu), % 0 to 0.25
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0 to 0.4
0 to 0.2
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0.4 to 0.8
0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.1
Silicon (Si), % 0 to 0.25
0
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0.4 to 0.8
0
Zirconium (Zr), % 0
94.7 to 100
Residuals, % 0 to 0.15
0