5070 Aluminum vs. C97800 Nickel Silver

5070 aluminum belongs to the aluminum alloys classification, while C97800 nickel silver belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5070 aluminum and the bottom bar is C97800 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
130
Elongation at Break, % 20
10
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
48
Tensile Strength: Ultimate (UTS), MPa 300
370
Tensile Strength: Yield (Proof), MPa 140
170

Thermal Properties

Latent Heat of Fusion, J/g 390
220
Maximum Temperature: Mechanical, °C 190
230
Melting Completion (Liquidus), °C 640
1180
Melting Onset (Solidus), °C 550
1140
Specific Heat Capacity, J/kg-K 900
390
Thermal Conductivity, W/m-K 130
25
Thermal Expansion, µm/m-K 24
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 31
4.0
Electrical Conductivity: Equal Weight (Specific), % IACS 100
4.1

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
40
Density, g/cm3 2.7
8.8
Embodied Carbon, kg CO2/kg material 8.8
5.1
Embodied Energy, MJ/kg 150
76
Embodied Water, L/kg 1170
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 51
31
Resilience: Unit (Modulus of Resilience), kJ/m3 150
120
Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 50
19
Strength to Weight: Axial, points 31
12
Strength to Weight: Bending, points 37
13
Thermal Diffusivity, mm2/s 53
7.3
Thermal Shock Resistance, points 14
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 92.4 to 95.7
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.25
64 to 67
Iron (Fe), % 0 to 0.4
0 to 1.5
Lead (Pb), % 0
1.0 to 2.5
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0.4 to 0.8
0
Nickel (Ni), % 0
24 to 27
Phosphorus (P), % 0
0 to 0.050
Silicon (Si), % 0 to 0.25
0 to 0.15
Sulfur (S), % 0
0 to 0.080
Tin (Sn), % 0
4.0 to 5.5
Titanium (Ti), % 0 to 0.15
0
Zinc (Zn), % 0.4 to 0.8
1.0 to 4.0
Residuals, % 0 to 0.15
0 to 0.4