5083 Aluminum vs. 6018 Aluminum
Both 5083 aluminum and 6018 aluminum are aluminum alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 5083 aluminum and the bottom bar is 6018 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 69 |
| Elongation at Break, % | 1.1 to 17 | |
| 9.0 to 9.1 |
| Fatigue Strength, MPa | 93 to 190 | |
| 85 to 89 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 170 to 220 | |
| 170 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 390 | |
| 290 to 300 |
| Tensile Strength: Yield (Proof), MPa | 110 to 340 | |
| 220 to 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 160 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 580 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 890 |
| Thermal Conductivity, W/m-K | 120 | |
| 170 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 44 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 96 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.7 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1170 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 42 | |
| 24 to 25 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 95 to 860 | |
| 360 to 380 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 48 |
| Strength to Weight: Axial, points | 29 to 40 | |
| 28 to 29 |
| Strength to Weight: Bending, points | 36 to 44 | |
| 34 to 35 |
| Thermal Diffusivity, mm2/s | 48 | |
| 65 |
| Thermal Shock Resistance, points | 12 to 17 | |
| 13 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 92.4 to 95.6 | |
| 93.1 to 97.8 |
| Bismuth (Bi), % | 0 | |
| 0.4 to 0.7 |
| Chromium (Cr), % | 0.050 to 0.25 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.1 | |
| 0.15 to 0.4 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.7 |
| Lead (Pb), % | 0 | |
| 0.4 to 1.2 |
| Magnesium (Mg), % | 4.0 to 4.9 | |
| 0.6 to 1.2 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0.3 to 0.8 |
| Silicon (Si), % | 0 to 0.4 | |
| 0.5 to 1.2 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |