50Cr-50Ni-Cb Alloy vs. AWS BAg-24

Both 50Cr-50Ni-Cb alloy and AWS BAg-24 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is 50Cr-50Ni-Cb alloy and the bottom bar is AWS BAg-24.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
87
Poisson's Ratio 0.26
0.33
Shear Modulus, GPa 84
33
Tensile Strength: Ultimate (UTS), MPa 620
150

Thermal Properties

Latent Heat of Fusion, J/g 350
130
Specific Heat Capacity, J/kg-K 480
310
Thermal Expansion, µm/m-K 15
21

Otherwise Unclassified Properties

Density, g/cm3 8.0
9.0
Embodied Carbon, kg CO2/kg material 9.2
49
Embodied Energy, MJ/kg 130
770

Common Calculations

Stiffness to Weight: Axial, points 15
5.3
Stiffness to Weight: Bending, points 25
16
Strength to Weight: Axial, points 21
4.6
Strength to Weight: Bending, points 20
6.9
Thermal Shock Resistance, points 14
5.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.25
0
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 47 to 52
0
Copper (Cu), % 0
19 to 21
Iron (Fe), % 0 to 1.0
0
Manganese (Mn), % 0 to 0.3
0
Nickel (Ni), % 43.3 to 51.6
1.5 to 2.5
Niobium (Nb), % 1.4 to 1.7
0
Nitrogen (N), % 0 to 0.16
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
49 to 51
Sulfur (S), % 0 to 0.020
0
Titanium (Ti), % 0 to 0.5
0
Zinc (Zn), % 0
26 to 30
Residuals, % 0
0 to 0.15