50Cr-50Ni-Cb Alloy vs. Sintered 2014 Aluminum

50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals classification, while sintered 2014 aluminum belongs to the aluminum alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 50Cr-50Ni-Cb alloy and the bottom bar is sintered 2014 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
70
Elongation at Break, % 5.6
0.5 to 3.0
Poisson's Ratio 0.26
0.33
Shear Modulus, GPa 84
26
Tensile Strength: Ultimate (UTS), MPa 620
140 to 290
Tensile Strength: Yield (Proof), MPa 390
97 to 280

Thermal Properties

Latent Heat of Fusion, J/g 350
390
Specific Heat Capacity, J/kg-K 480
880
Thermal Expansion, µm/m-K 15
23

Otherwise Unclassified Properties

Base Metal Price, % relative 60
10
Density, g/cm3 8.0
2.9
Embodied Carbon, kg CO2/kg material 9.2
8.0
Embodied Energy, MJ/kg 130
150
Embodied Water, L/kg 350
1150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 30
1.0 to 5.7
Resilience: Unit (Modulus of Resilience), kJ/m3 370
68 to 560
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
47
Strength to Weight: Axial, points 21
13 to 27
Strength to Weight: Bending, points 20
20 to 33
Thermal Shock Resistance, points 14
6.2 to 13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.25
91.5 to 96.3
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 47 to 52
0
Copper (Cu), % 0
3.5 to 5.0
Iron (Fe), % 0 to 1.0
0
Magnesium (Mg), % 0
0.2 to 0.8
Manganese (Mn), % 0 to 0.3
0
Nickel (Ni), % 43.3 to 51.6
0
Niobium (Nb), % 1.4 to 1.7
0
Nitrogen (N), % 0 to 0.16
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0 to 1.2
Sulfur (S), % 0 to 0.020
0
Titanium (Ti), % 0 to 0.5
0
Residuals, % 0
0 to 1.5