50Cr-50Ni-Cb Alloy vs. C61300 Bronze
50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals classification, while C61300 bronze belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is 50Cr-50Ni-Cb alloy and the bottom bar is C61300 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Elongation at Break, % | 5.6 | |
| 34 to 40 |
| Poisson's Ratio | 0.26 | |
| 0.34 |
| Shear Modulus, GPa | 84 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 550 to 580 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 420 |
| Thermal Expansion, µm/m-K | 15 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 29 |
| Density, g/cm3 | 8.0 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 9.2 | |
| 3.0 |
| Embodied Energy, MJ/kg | 130 | |
| 49 |
| Embodied Water, L/kg | 350 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 | |
| 150 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 230 to 410 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 21 | |
| 18 to 19 |
| Strength to Weight: Bending, points | 20 | |
| 18 |
| Thermal Shock Resistance, points | 14 | |
| 19 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.25 | |
| 6.0 to 7.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 47 to 52 | |
| 0 |
| Copper (Cu), % | 0 | |
| 88 to 91.8 |
| Iron (Fe), % | 0 to 1.0 | |
| 2.0 to 3.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 to 0.2 |
| Nickel (Ni), % | 43.3 to 51.6 | |
| 0 to 0.15 |
| Niobium (Nb), % | 1.4 to 1.7 | |
| 0 |
| Nitrogen (N), % | 0 to 0.16 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.2 to 0.5 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.2 |