514.0 Aluminum vs. 520.0 Aluminum
Both 514.0 aluminum and 520.0 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common.
For each property being compared, the top bar is 514.0 aluminum and the bottom bar is 520.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 50 | |
| 75 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 66 |
| Elongation at Break, % | 7.3 | |
| 14 |
| Fatigue Strength, MPa | 48 | |
| 55 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 25 | |
| 25 |
| Shear Strength, MPa | 140 | |
| 230 |
| Tensile Strength: Ultimate (UTS), MPa | 180 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 74 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 600 |
| Melting Onset (Solidus), °C | 610 | |
| 480 |
| Solidification (Pattern Maker's) Shrinkage, % | 1.3 | |
| 0.8 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 910 |
| Thermal Conductivity, W/m-K | 140 | |
| 87 |
| Thermal Expansion, µm/m-K | 24 | |
| 25 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 21 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 72 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 9.8 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1180 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 | |
| 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 41 | |
| 230 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 52 |
| Strength to Weight: Axial, points | 19 | |
| 35 |
| Strength to Weight: Bending, points | 26 | |
| 41 |
| Thermal Diffusivity, mm2/s | 57 | |
| 37 |
| Thermal Shock Resistance, points | 7.9 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 93.6 to 96.5 | |
| 87.9 to 90.5 |
| Copper (Cu), % | 0 to 0.15 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 3.5 to 4.5 | |
| 9.5 to 10.6 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 0.15 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.15 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |