515.0 Aluminum vs. 5254 Aluminum
Both 515.0 aluminum and 5254 aluminum are aluminum alloys. They have a very high 99% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is 515.0 aluminum and the bottom bar is 5254 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 68 |
| Elongation at Break, % | 10 | |
| 3.4 to 22 |
| Fatigue Strength, MPa | 130 | |
| 110 to 160 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 190 | |
| 150 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 240 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 470 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 190 |
| Melting Completion (Liquidus), °C | 620 | |
| 640 |
| Melting Onset (Solidus), °C | 620 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.6 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.8 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1120 | |
| 1180 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 52 | |
| 51 |
| Strength to Weight: Axial, points | 30 | |
| 25 to 37 |
| Strength to Weight: Bending, points | 36 | |
| 32 to 41 |
| Thermal Shock Resistance, points | 13 | |
| 10 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 93.6 to 96.6 | |
| 94.4 to 96.8 |
| Chromium (Cr), % | 0 | |
| 0.15 to 0.35 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 1.3 | |
| 0 to 0.45 |
| Magnesium (Mg), % | 2.5 to 4.0 | |
| 3.1 to 3.9 |
| Manganese (Mn), % | 0.4 to 0.6 | |
| 0 to 0.010 |
| Silicon (Si), % | 0.5 to 10 | |
| 0 to 0.45 |
| Titanium (Ti), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |