5154-H24 Aluminum vs. 5449-H24 Aluminum
Both 5154-H24 aluminum and 5449-H24 aluminum are aluminum alloys. Both are furnished in the H24 temper. They have a very high 99% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 5154-H24 aluminum and the bottom bar is 5449-H24 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 68 | |
69 |
Elongation at Break, % | 7.8 | |
7.3 |
Fatigue Strength, MPa | 130 | |
99 |
Poisson's Ratio | 0.33 | |
0.33 |
Shear Modulus, GPa | 26 | |
26 |
Shear Strength, MPa | 170 | |
150 |
Tensile Strength: Ultimate (UTS), MPa | 300 | |
260 |
Tensile Strength: Yield (Proof), MPa | 230 | |
180 |
Thermal Properties
Latent Heat of Fusion, J/g | 400 | |
400 |
Maximum Temperature: Mechanical, °C | 190 | |
190 |
Melting Completion (Liquidus), °C | 640 | |
650 |
Melting Onset (Solidus), °C | 590 | |
590 |
Specific Heat Capacity, J/kg-K | 900 | |
900 |
Thermal Conductivity, W/m-K | 130 | |
140 |
Thermal Expansion, µm/m-K | 24 | |
23 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 32 | |
35 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
110 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 9.5 | |
9.5 |
Density, g/cm3 | 2.7 | |
2.8 |
Embodied Carbon, kg CO2/kg material | 8.8 | |
8.5 |
Embodied Energy, MJ/kg | 150 | |
150 |
Embodied Water, L/kg | 1180 | |
1180 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 | |
17 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 390 | |
240 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 51 | |
50 |
Strength to Weight: Axial, points | 30 | |
26 |
Strength to Weight: Bending, points | 37 | |
33 |
Thermal Diffusivity, mm2/s | 52 | |
56 |
Thermal Shock Resistance, points | 13 | |
11 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % | 94.4 to 96.8 | |
94.1 to 97.8 |
Chromium (Cr), % | 0.15 to 0.35 | |
0 to 0.3 |
Copper (Cu), % | 0 to 0.1 | |
0 to 0.3 |
Iron (Fe), % | 0 to 0.4 | |
0 to 0.7 |
Magnesium (Mg), % | 3.1 to 3.9 | |
1.6 to 2.6 |
Manganese (Mn), % | 0 to 0.1 | |
0.6 to 1.1 |
Silicon (Si), % | 0 to 0.25 | |
0 to 0.4 |
Titanium (Ti), % | 0 to 0.2 | |
0 to 0.1 |
Zinc (Zn), % | 0 to 0.2 | |
0 to 0.3 |
Residuals, % | 0 to 0.15 | |
0 to 0.15 |