5182 Aluminum vs. 1070 Aluminum

Both 5182 aluminum and 1070 aluminum are aluminum alloys. They have a moderately high 95% of their average alloy composition in common.

For each property being compared, the top bar is 5182 aluminum and the bottom bar is 1070 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
68
Elongation at Break, % 1.1 to 12
4.5 to 39
Fatigue Strength, MPa 100 to 130
22 to 49
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 25
26
Shear Strength, MPa 170 to 240
48 to 79
Tensile Strength: Ultimate (UTS), MPa 280 to 420
73 to 140
Tensile Strength: Yield (Proof), MPa 130 to 360
17 to 120

Thermal Properties

Latent Heat of Fusion, J/g 390
400
Maximum Temperature: Mechanical, °C 180
170
Melting Completion (Liquidus), °C 640
640
Melting Onset (Solidus), °C 590
640
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 130
230
Thermal Expansion, µm/m-K 24
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
61
Electrical Conductivity: Equal Weight (Specific), % IACS 94
200

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.7
Embodied Carbon, kg CO2/kg material 8.9
8.3
Embodied Energy, MJ/kg 150
160
Embodied Water, L/kg 1180
1200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.6 to 49
4.8 to 21
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 950
2.1 to 110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 51
50
Strength to Weight: Axial, points 29 to 44
7.5 to 14
Strength to Weight: Bending, points 36 to 47
14 to 22
Thermal Diffusivity, mm2/s 53
94
Thermal Shock Resistance, points 12 to 19
3.3 to 6.1

Alloy Composition

Aluminum (Al), % 93.2 to 95.8
99.7 to 100
Chromium (Cr), % 0 to 0.1
0
Copper (Cu), % 0 to 0.15
0 to 0.040
Iron (Fe), % 0 to 0.35
0 to 0.25
Magnesium (Mg), % 4.0 to 5.0
0 to 0.030
Manganese (Mn), % 0.2 to 0.5
0 to 0.030
Silicon (Si), % 0 to 0.2
0 to 0.2
Titanium (Ti), % 0 to 0.1
0 to 0.030
Vanadium (V), % 0
0 to 0.050
Zinc (Zn), % 0 to 0.25
0 to 0.040
Residuals, % 0 to 0.15
0 to 0.030

Comparable Variants