5182 Aluminum vs. 1100A Aluminum

Both 5182 aluminum and 1100A aluminum are aluminum alloys. They have a very high 95% of their average alloy composition in common.

For each property being compared, the top bar is 5182 aluminum and the bottom bar is 1100A aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
69
Elongation at Break, % 1.1 to 12
4.5 to 34
Fatigue Strength, MPa 100 to 130
35 to 74
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 25
26
Shear Strength, MPa 170 to 240
59 to 99
Tensile Strength: Ultimate (UTS), MPa 280 to 420
89 to 170
Tensile Strength: Yield (Proof), MPa 130 to 360
29 to 150

Thermal Properties

Latent Heat of Fusion, J/g 390
400
Maximum Temperature: Mechanical, °C 180
170
Melting Completion (Liquidus), °C 640
640
Melting Onset (Solidus), °C 590
640
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 130
230
Thermal Expansion, µm/m-K 24
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
60
Electrical Conductivity: Equal Weight (Specific), % IACS 94
200

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.7
Embodied Carbon, kg CO2/kg material 8.9
8.2
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1180
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.6 to 49
6.4 to 23
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 950
5.9 to 150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 51
50
Strength to Weight: Axial, points 29 to 44
9.1 to 17
Strength to Weight: Bending, points 36 to 47
16 to 25
Thermal Diffusivity, mm2/s 53
93
Thermal Shock Resistance, points 12 to 19
4.0 to 7.6

Alloy Composition

Aluminum (Al), % 93.2 to 95.8
99 to 100
Chromium (Cr), % 0 to 0.1
0
Copper (Cu), % 0 to 0.15
0.050 to 0.2
Iron (Fe), % 0 to 0.35
0 to 1.0
Magnesium (Mg), % 4.0 to 5.0
0 to 0.1
Manganese (Mn), % 0.2 to 0.5
0 to 0.050
Silicon (Si), % 0 to 0.2
0 to 1.0
Titanium (Ti), % 0 to 0.1
0 to 0.1
Zinc (Zn), % 0 to 0.25
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15

Comparable Variants