5182 Aluminum vs. A444.0 Aluminum

Both 5182 aluminum and A444.0 aluminum are aluminum alloys. They have a moderately high 93% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is 5182 aluminum and the bottom bar is A444.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
70
Elongation at Break, % 1.1 to 12
18
Fatigue Strength, MPa 100 to 130
37
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 25
26
Tensile Strength: Ultimate (UTS), MPa 280 to 420
160
Tensile Strength: Yield (Proof), MPa 130 to 360
66

Thermal Properties

Latent Heat of Fusion, J/g 390
500
Maximum Temperature: Mechanical, °C 180
170
Melting Completion (Liquidus), °C 640
630
Melting Onset (Solidus), °C 590
590
Specific Heat Capacity, J/kg-K 900
900
Thermal Conductivity, W/m-K 130
160
Thermal Expansion, µm/m-K 24
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
41
Electrical Conductivity: Equal Weight (Specific), % IACS 94
140

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.6
Embodied Carbon, kg CO2/kg material 8.9
7.9
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1180
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.6 to 49
24
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 950
31
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 51
53
Strength to Weight: Axial, points 29 to 44
17
Strength to Weight: Bending, points 36 to 47
25
Thermal Diffusivity, mm2/s 53
68
Thermal Shock Resistance, points 12 to 19
7.3

Alloy Composition

Aluminum (Al), % 93.2 to 95.8
91.6 to 93.5
Chromium (Cr), % 0 to 0.1
0
Copper (Cu), % 0 to 0.15
0 to 0.1
Iron (Fe), % 0 to 0.35
0 to 0.2
Magnesium (Mg), % 4.0 to 5.0
0 to 0.050
Manganese (Mn), % 0.2 to 0.5
0 to 0.1
Silicon (Si), % 0 to 0.2
6.5 to 7.5
Titanium (Ti), % 0 to 0.1
0 to 0.2
Zinc (Zn), % 0 to 0.25
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.15