5182 Aluminum vs. EN AC-51100 Aluminum
Both 5182 aluminum and EN AC-51100 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 5182 aluminum and the bottom bar is EN AC-51100 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 1.1 to 12 | |
| 4.5 |
| Fatigue Strength, MPa | 100 to 130 | |
| 58 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 25 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 420 | |
| 160 |
| Tensile Strength: Yield (Proof), MPa | 130 to 360 | |
| 80 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 590 | |
| 620 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 130 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 94 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 8.7 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.6 to 49 | |
| 6.0 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 950 | |
| 47 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 51 |
| Strength to Weight: Axial, points | 29 to 44 | |
| 17 |
| Strength to Weight: Bending, points | 36 to 47 | |
| 25 |
| Thermal Diffusivity, mm2/s | 53 | |
| 53 |
| Thermal Shock Resistance, points | 12 to 19 | |
| 7.3 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 93.2 to 95.8 | |
| 94.5 to 97.5 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 to 0.15 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.55 |
| Magnesium (Mg), % | 4.0 to 5.0 | |
| 2.5 to 3.5 |
| Manganese (Mn), % | 0.2 to 0.5 | |
| 0 to 0.45 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.55 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |