5251 Aluminum vs. 7475 Aluminum
Both 5251 aluminum and 7475 aluminum are aluminum alloys. They have a moderately high 93% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 5251 aluminum and the bottom bar is 7475 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 70 |
| Elongation at Break, % | 2.0 to 19 | |
| 10 to 12 |
| Fatigue Strength, MPa | 59 to 110 | |
| 190 to 210 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 110 to 160 | |
| 320 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 280 | |
| 530 to 590 |
| Tensile Strength: Yield (Proof), MPa | 67 to 250 | |
| 440 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 650 | |
| 640 |
| Melting Onset (Solidus), °C | 610 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 870 |
| Thermal Conductivity, W/m-K | 150 | |
| 140 to 160 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 37 | |
| 33 to 42 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 98 to 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.7 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.4 to 27 | |
| 53 to 68 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 33 to 450 | |
| 1390 to 1920 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 46 |
| Strength to Weight: Axial, points | 18 to 29 | |
| 49 to 55 |
| Strength to Weight: Bending, points | 26 to 35 | |
| 48 to 52 |
| Thermal Diffusivity, mm2/s | 61 | |
| 53 to 63 |
| Thermal Shock Resistance, points | 7.9 to 13 | |
| 23 to 26 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 95.5 to 98.2 | |
| 88.6 to 91.6 |
| Chromium (Cr), % | 0 to 0.15 | |
| 0.18 to 0.25 |
| Copper (Cu), % | 0 to 0.15 | |
| 1.2 to 1.9 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.12 |
| Magnesium (Mg), % | 1.7 to 2.4 | |
| 1.9 to 2.6 |
| Manganese (Mn), % | 0.1 to 0.5 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.060 |
| Zinc (Zn), % | 0 to 0.15 | |
| 5.1 to 6.2 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |