5252 Aluminum vs. A357.0 Aluminum
Both 5252 aluminum and A357.0 aluminum are aluminum alloys. They have a moderately high 93% of their average alloy composition in common.
For each property being compared, the top bar is 5252 aluminum and the bottom bar is A357.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 68 to 75 | |
| 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 70 |
| Elongation at Break, % | 4.5 to 11 | |
| 3.7 |
| Fatigue Strength, MPa | 100 to 110 | |
| 100 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 25 | |
| 26 |
| Shear Strength, MPa | 140 to 160 | |
| 240 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 290 | |
| 350 |
| Tensile Strength: Yield (Proof), MPa | 170 to 240 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 500 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 170 |
| Melting Completion (Liquidus), °C | 650 | |
| 610 |
| Melting Onset (Solidus), °C | 610 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 910 | |
| 900 |
| Thermal Conductivity, W/m-K | 140 | |
| 160 |
| Thermal Expansion, µm/m-K | 24 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 8.2 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 23 | |
| 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 430 | |
| 520 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 51 | |
| 53 |
| Strength to Weight: Axial, points | 23 to 30 | |
| 38 |
| Strength to Weight: Bending, points | 31 to 36 | |
| 43 |
| Thermal Diffusivity, mm2/s | 57 | |
| 68 |
| Thermal Shock Resistance, points | 10 to 13 | |
| 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 96.6 to 97.8 | |
| 90.8 to 93 |
| Beryllium (Be), % | 0 | |
| 0.040 to 0.070 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.2 |
| Magnesium (Mg), % | 2.2 to 2.8 | |
| 0.4 to 0.7 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.080 | |
| 6.5 to 7.5 |
| Titanium (Ti), % | 0 | |
| 0.040 to 0.2 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.050 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.1 | |
| 0 to 0.15 |