5457 Aluminum vs. 513.0 Aluminum
Both 5457 aluminum and 513.0 aluminum are aluminum alloys. They have a moderately high 95% of their average alloy composition in common.
For each property being compared, the top bar is 5457 aluminum and the bottom bar is 513.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 32 to 55 | |
| 55 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 6.0 to 22 | |
| 5.7 |
| Fatigue Strength, MPa | 55 to 98 | |
| 97 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 85 to 130 | |
| 170 |
| Tensile Strength: Ultimate (UTS), MPa | 130 to 210 | |
| 200 |
| Tensile Strength: Yield (Proof), MPa | 50 to 190 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 170 |
| Melting Completion (Liquidus), °C | 660 | |
| 640 |
| Melting Onset (Solidus), °C | 630 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 180 | |
| 130 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 46 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 150 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.8 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1190 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 23 | |
| 9.8 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 18 to 250 | |
| 100 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 13 to 21 | |
| 20 |
| Strength to Weight: Bending, points | 21 to 28 | |
| 28 |
| Thermal Diffusivity, mm2/s | 72 | |
| 54 |
| Thermal Shock Resistance, points | 5.7 to 9.0 | |
| 8.8 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 97.8 to 99.05 | |
| 91.9 to 95.1 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 0.8 to 1.2 | |
| 3.5 to 4.5 |
| Manganese (Mn), % | 0.15 to 0.45 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 to 0.3 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.050 | |
| 1.4 to 2.2 |
| Residuals, % | 0 to 0.1 | |
| 0 to 0.15 |