MakeItFrom.com
Menu (ESC)

5457 Aluminum vs. R31233 Cobalt

5457 aluminum belongs to the aluminum alloys classification, while R31233 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5457 aluminum and the bottom bar is R31233 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
220
Elongation at Break, % 6.0 to 22
17
Fatigue Strength, MPa 55 to 98
220
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
85
Tensile Strength: Ultimate (UTS), MPa 130 to 210
1020
Tensile Strength: Yield (Proof), MPa 50 to 190
420

Thermal Properties

Latent Heat of Fusion, J/g 400
320
Melting Completion (Liquidus), °C 660
1350
Melting Onset (Solidus), °C 630
1330
Specific Heat Capacity, J/kg-K 900
440
Thermal Conductivity, W/m-K 180
12
Thermal Expansion, µm/m-K 24
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 46
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 150
2.1

Otherwise Unclassified Properties

Density, g/cm3 2.7
8.6
Embodied Carbon, kg CO2/kg material 8.4
8.4
Embodied Energy, MJ/kg 160
110
Embodied Water, L/kg 1190
480

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12 to 23
140
Resilience: Unit (Modulus of Resilience), kJ/m3 18 to 250
410
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
23
Strength to Weight: Axial, points 13 to 21
33
Strength to Weight: Bending, points 21 to 28
26
Thermal Diffusivity, mm2/s 72
3.2
Thermal Shock Resistance, points 5.7 to 9.0
25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 97.8 to 99.05
0
Boron (B), % 0
0 to 0.015
Carbon (C), % 0
0.020 to 0.1
Chromium (Cr), % 0
23.5 to 27.5
Cobalt (Co), % 0
44.7 to 63.3
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 0 to 0.1
1.0 to 5.0
Magnesium (Mg), % 0.8 to 1.2
0
Manganese (Mn), % 0.15 to 0.45
0.1 to 1.5
Molybdenum (Mo), % 0
4.0 to 6.0
Nickel (Ni), % 0
7.0 to 11
Nitrogen (N), % 0
0.030 to 0.12
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.080
0.050 to 1.0
Sulfur (S), % 0
0 to 0.020
Tungsten (W), % 0
1.0 to 3.0
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0 to 0.050
0
Residuals, % 0 to 0.1
0