5652 Aluminum vs. EN AC-46200 Aluminum
Both 5652 aluminum and EN AC-46200 aluminum are aluminum alloys. They have 87% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 5652 aluminum and the bottom bar is EN AC-46200 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 47 to 77 | |
| 82 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 73 |
| Elongation at Break, % | 6.8 to 25 | |
| 1.1 |
| Fatigue Strength, MPa | 60 to 140 | |
| 87 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 290 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 74 to 260 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 510 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 170 |
| Melting Completion (Liquidus), °C | 650 | |
| 620 |
| Melting Onset (Solidus), °C | 610 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 880 |
| Thermal Conductivity, W/m-K | 140 | |
| 110 |
| Thermal Expansion, µm/m-K | 24 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 88 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.7 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.6 | |
| 7.7 |
| Embodied Energy, MJ/kg | 150 | |
| 140 |
| Embodied Water, L/kg | 1190 | |
| 1060 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 39 | |
| 2.0 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 40 to 480 | |
| 110 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 50 |
| Strength to Weight: Axial, points | 20 to 30 | |
| 21 |
| Strength to Weight: Bending, points | 27 to 36 | |
| 28 |
| Thermal Diffusivity, mm2/s | 57 | |
| 44 |
| Thermal Shock Resistance, points | 8.4 to 13 | |
| 9.5 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 95.8 to 97.7 | |
| 82.6 to 90.3 |
| Chromium (Cr), % | 0.15 to 0.35 | |
| 0 |
| Copper (Cu), % | 0 to 0.040 | |
| 2.0 to 3.5 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.8 |
| Lead (Pb), % | 0 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 2.2 to 2.8 | |
| 0.050 to 0.55 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0.15 to 0.65 |
| Nickel (Ni), % | 0 | |
| 0 to 0.35 |
| Silicon (Si), % | 0 to 0.4 | |
| 7.5 to 9.5 |
| Tin (Sn), % | 0 | |
| 0 to 0.15 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 1.2 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.25 |