5657 Aluminum vs. 5449 Aluminum
Both 5657 aluminum and 5449 aluminum are aluminum alloys. They have a very high 97% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 5657 aluminum and the bottom bar is 5449 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 69 |
| Elongation at Break, % | 6.6 to 15 | |
| 4.0 to 17 |
| Fatigue Strength, MPa | 74 to 88 | |
| 78 to 120 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 92 to 110 | |
| 130 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 150 to 200 | |
| 210 to 330 |
| Tensile Strength: Yield (Proof), MPa | 140 to 170 | |
| 91 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 190 |
| Melting Completion (Liquidus), °C | 660 | |
| 650 |
| Melting Onset (Solidus), °C | 640 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 210 | |
| 140 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 54 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 180 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.5 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1200 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.7 to 27 | |
| 12 to 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 200 | |
| 60 to 480 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 22 to 33 |
| Strength to Weight: Bending, points | 23 to 28 | |
| 29 to 39 |
| Thermal Diffusivity, mm2/s | 84 | |
| 56 |
| Thermal Shock Resistance, points | 6.7 to 8.6 | |
| 9.4 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 98.5 to 99.4 | |
| 94.1 to 97.8 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.3 |
| Gallium (Ga), % | 0 to 0.030 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0.6 to 1.0 | |
| 1.6 to 2.6 |
| Manganese (Mn), % | 0 to 0.030 | |
| 0.6 to 1.1 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.050 | |
| 0 to 0.3 |
| Residuals, % | 0 to 0.050 | |
| 0 to 0.15 |