5754 Aluminum vs. 5754-H12 Aluminum
5754-H12 aluminum is a variant of 5754 aluminum. The properties of the parent material encompass the values of all of its variants.
For each property being compared, the top bar is 5754 aluminum and the bottom bar is 5754-H12 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 52 to 88 | |
| 66 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 2.0 to 19 | |
| 5.5 |
| Fatigue Strength, MPa | 66 to 140 | |
| 140 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 120 to 190 | |
| 140 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 330 | |
| 240 |
| Tensile Strength: Yield (Proof), MPa | 80 to 280 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 190 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 600 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 130 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 | |
| 33 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 8.7 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.1 to 32 | |
| 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 47 to 580 | |
| 270 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 21 to 34 | |
| 25 |
| Strength to Weight: Bending, points | 28 to 39 | |
| 32 |
| Thermal Diffusivity, mm2/s | 54 | |
| 54 |
| Thermal Shock Resistance, points | 8.9 to 14 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 94.2 to 97.4 | |
| 94.2 to 97.4 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 2.6 to 3.6 | |
| 2.6 to 3.6 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.5 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |