60Pd-40Ag Alloy vs. ASTM B522 Class II
Both 60Pd-40Ag alloy and ASTM B522 class II are otherwise unclassified metals. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is 60Pd-40Ag alloy and the bottom bar is ASTM B522 class II.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 96 |
| Elongation at Break, % | 1.1 to 28 | |
| 1.1 to 28 |
| Knoop Hardness | 110 to 220 | |
| 88 to 150 |
| Poisson's Ratio | 0.38 | |
| 0.41 |
| Shear Modulus, GPa | 37 | |
| 34 |
| Shear Strength, MPa | 220 to 350 | |
| 180 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 720 | |
| 280 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 77 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1030 |
| Melting Onset (Solidus), °C | 1310 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 160 |
| Thermal Expansion, µm/m-K | 15 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.1 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 5.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.9 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 14 | |
| 8.9 |
| Strength to Weight: Axial, points | 8.4 to 18 | |
| 4.4 to 7.8 |
| Strength to Weight: Bending, points | 9.6 to 16 | |
| 5.5 to 8.0 |
| Thermal Shock Resistance, points | 16 to 34 | |
| 13 to 24 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Gold (Au), % | 0 | |
| 68.5 to 69.5 |
| Palladium (Pd), % | 59.5 to 60.9 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 5.5 to 6.5 |
| Silver (Ag), % | 39.1 to 40.5 | |
| 24.5 to 25.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.26 |