60Pd-40Ag Alloy vs. Solder Alloy 104

Both 60Pd-40Ag alloy and solder alloy 104 are otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is 60Pd-40Ag alloy and the bottom bar is solder alloy 104.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
37
Elongation at Break, % 1.1 to 28
46
Poisson's Ratio 0.38
0.39
Shear Modulus, GPa 37
13
Tensile Strength: Ultimate (UTS), MPa 340 to 720
51

Thermal Properties

Latent Heat of Fusion, J/g 140
45
Melting Completion (Liquidus), °C 1360
190
Melting Onset (Solidus), °C 1310
180
Specific Heat Capacity, J/kg-K 240
180
Thermal Conductivity, W/m-K 29
50
Thermal Expansion, µm/m-K 15
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.1
11
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
11

Otherwise Unclassified Properties

Density, g/cm3 11
8.9

Common Calculations

Stiffness to Weight: Axial, points 4.9
2.3
Stiffness to Weight: Bending, points 14
12
Strength to Weight: Axial, points 8.4 to 18
1.6
Strength to Weight: Bending, points 9.6 to 16
3.4
Thermal Diffusivity, mm2/s 11
30
Thermal Shock Resistance, points 16 to 34
4.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.050
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 0 to 0.1
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
39 to 40.5
Nickel (Ni), % 0
0 to 0.010
Palladium (Pd), % 59.5 to 60.9
0
Silver (Ag), % 39.1 to 40.5
0 to 0.1
Tin (Sn), % 0
59.5 to 60.5
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.3
0