60Pd-40Ag Alloy vs. Solder Alloy 171

Both 60Pd-40Ag alloy and solder alloy 171 are otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is 60Pd-40Ag alloy and the bottom bar is solder alloy 171.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
38
Elongation at Break, % 1.1 to 28
45
Poisson's Ratio 0.38
0.39
Shear Modulus, GPa 37
14
Tensile Strength: Ultimate (UTS), MPa 340 to 720
48

Thermal Properties

Latent Heat of Fusion, J/g 140
47
Melting Completion (Liquidus), °C 1360
180
Melting Onset (Solidus), °C 1310
180
Specific Heat Capacity, J/kg-K 240
190
Thermal Conductivity, W/m-K 29
50
Thermal Expansion, µm/m-K 15
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.1
12
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
12

Otherwise Unclassified Properties

Density, g/cm3 11
8.8

Common Calculations

Stiffness to Weight: Axial, points 4.9
2.4
Stiffness to Weight: Bending, points 14
13
Strength to Weight: Axial, points 8.4 to 18
1.5
Strength to Weight: Bending, points 9.6 to 16
3.3
Thermal Diffusivity, mm2/s 11
30
Thermal Shock Resistance, points 16 to 34
3.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 0 to 0.1
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
34.7 to 36.7
Nickel (Ni), % 0
0 to 0.010
Palladium (Pd), % 59.5 to 60.9
0
Silver (Ag), % 39.1 to 40.5
1.8 to 2.2
Tin (Sn), % 0
61.5 to 62.5
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.3
0